固体润滑国家重点实验室（LSL）知识库

The corrosion−wear behavior of a nanocrystalline Fe₈₈Si₁₂ alloy disc coupled with a Si₃N₄ ball was investigated in acid (pH 3) and alkaline (pH 9) aqueous solutions. The dry wear was also measured for reference. The average friction coefficient of Fe₈₈Si₁₂ alloy in the pH 9 solution was approximately 0.2, which was lower than those observed for Fe₈₈Si₁₂ alloy in the pH 3 solution and in the case of dry wear. The fluctuation of the friction coefficient of samples subjected to the pH 9 solution also showed similar characteristics. The wear rate in the pH 9 solution slightly increased with increasing applied load. The wear rate was approximately one order of magnitude less than that in the pH 3 solution and was far lower than that in the case of dry wear, especially at high applied load. The wear traces of Fe₈₈Si₁₂ alloy under different wear conditions were examined and analyzed by scanning electron microscopy, energy-dispersive X-ray spectroscopy, and X-ray photoelectron spectroscopy. The results indicated that the tribo-chemical reactions that involve oxidation of the worn surface and hydrolysis of the Si₃N₄ ball in the acid solution were restricted in the pH 9 aqueous solution. Thus, water lubrication can effectively improve the wear resistance of nanocrystalline Fe₈₈Si₁₂ alloy in the pH 9 aqueous solution.