The effect of oxygen on the tribological behavior of CrNiMo steel | |
Department | 固体润滑国家重点实验室 |
Du SM(杜三明)1,2; Zhang YZ(张永振)2; Chen, Yue2; Liu WM(刘维民)1 | |
2012 | |
Source Publication | Industrial Lubrication and Tribology |
ISSN | 0036-8792 |
Volume | 64Issue:2-3Pages:71-76 |
Abstract | Purpose–The purpose of this paper is to study the friction and wear properties of CrNiMo steel pin against brass disk in different oxygen fractions. CrNiMo steel is currently widely used in industry and military fields for its excellent performance in some severe environments. The atmosphere and temperature are key factors affecting the wear behaviors of CrNiMo steel. The study aims to make better use of CrNiMo steel in different atmospheres. Design/methodology/approach–Friction and wear experiments were conducted using a pin‐on‐disk tribometer equipped in an atmosphere controllable chamber. The chamber allows switch between vacuum and gas mixtures of N2 and O2. The oxygen content was managed by magnetic coupling flow meter. The sliding speed of 1, 2, 3, 4 m/s and the applied sliding contact load of 5, 6.5, 8, 9.5 N were used in friction test. In order to obtain information on the wear mechanisms, the worn surface of the pin was examined by scanning electron microscopy and energy dispersive X‐ray spectroscopy. Findings–A close dependence is clearly shown of the friction and wear on the content of oxygen gas in elevated temperature. Increasing the content of oxygen in the atmosphere under higher normal load condition is beneficial to friction reduction of the steel/brass pair. Different wear mechanisms were found with a transition from the adhesive wear in nitrogen, to a mixed adhesion and oxidation wear when increasing the content of the oxygen in the atmosphere. Originality/value–This paper provides a reference for the similar steel used in severe environments. |
Keyword | Steel Brass Oxygen Friction Wear Atmosphere Dry Sliding Wear Mechanism |
Subject Area | 材料科学与物理化学 |
DOI | 10.1108/00368791211208660 |
Funding Organization | the 973 Program of China (Grant no. 2007CB607603) |
Indexed By | SCI |
If | 0.402 |
Language | 英语 |
Funding Project | 空间润滑材料组 |
compositor | 第一作者单位 |
Citation statistics | |
Document Type | 期刊论文 |
Identifier | http://ir.licp.cn/handle/362003/19533 |
Collection | 固体润滑国家重点实验室(LSL) |
Affiliation | 1.Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China 2.Henan Univ Sci & Technol, Coll Mat Sci & Engn, Grad Sch, Chinese Acad Sci, Luoyang, Peoples R China |
Recommended Citation GB/T 7714 | Du SM,Zhang YZ,Chen, Yue,et al. The effect of oxygen on the tribological behavior of CrNiMo steel[J]. Industrial Lubrication and Tribology,2012,64(2-3):71-76. |
APA | Du SM,Zhang YZ,Chen, Yue,&Liu WM.(2012).The effect of oxygen on the tribological behavior of CrNiMo steel.Industrial Lubrication and Tribology,64(2-3),71-76. |
MLA | Du SM,et al."The effect of oxygen on the tribological behavior of CrNiMo steel".Industrial Lubrication and Tribology 64.2-3(2012):71-76. |
Files in This Item: | ||||||
File Name/Size | DocType | Version | Access | License | ||
LZ01028596.pdf(4895KB) | 期刊论文 | 作者接受稿 | 开放获取 | CC BY-NC-SA | View Application Full Text |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment