| Direct synthesis and structural characteristics of ordered SBA-15 mesoporous silica containing tungsten oxides and tungsten carbides | |
| Department | 羰基合成与选择氧化国家重点实验室 |
Hu LH(胡林华); Ji SF(季生福); Jiang Z(江正); Song HL(宋焕玲) ; Wu PY(武平一); Liu QQ(刘倩倩)
| |
| 2007 | |
| Source Publication | Journal of Physical Chemistry C
 |
| ISSN | 1932-7447 |
| Volume | 111Issue:42Pages:15173-15184 |
| Abstract | A series of WO3-SBA-15 materials with different Si/W ratios have been hydrothermally synthesized using tetraethyl orthosilicate (TEOS) as silica precursor, ammonium paratungstate as tungsten precursor, and EO20- PO70EO20 (P123) as structure-directing reagent. After temperature-programmed carburization (TPC) in flowing CH4/H2 (20/80 v/v mixture), the materials were converted to the corresponding WxC-SBA-15 materials. The structure of the oxide and carbide materials has been characterized using X-ray diffraction (XRD), X-ray fluorescence (XRF), nitrogen adsorption-desorption measurements, 29Si magic-angle spinning (MAS) NMR spectroscopy, Fourier transform infrared (FTIR) spectroscopy, transmission electron microscopy (TEM), and thermogravimetric and differential scanning calorimetric analysis (TG-DSC) measurements. The results show that after hydrothermal synthesis using different amounts of tungsten and subsequent carburization, the materials retain the mesopore structure of SBA-15. When Si/W ) 30-15, the majority of the tungsten is dispersed in the channels of SBA-15 with the remainder being incorporated into the framework of SBA-15 with the formation of Si-O-W bonds. The tungsten carbide exists as a single W2C phase after carburization. At higher tungsten content (Si/W ) 7.5), the amount of tungsten in the framework of SBA-15 increases with the formation of both Si-O-W bonds and W-O-W bonds. The tungsten carbide formed after carburization exists as a mixture of W2C and WC phases. A model for the distribution of tungsten in SBA-15 is proposed involving three different tungsten species: R-W inside SBA-15 channels, â-W embedded in the internal surfaces of the SBA-15 channels, and ç-W inside the framework of SBA-15. After temperature-programmed carburization, R-W sites are transformed into W2C, whereas â-W sites afford WC; in contrast, ç-W sites show little change after carburization. |
| Subject Area | 物理化学 |
| Funding Organization | the National Natural Science Foundation of China (Grant No. 20473009);the National Basic Research Program of China (973 Program) (Grant No. 2006CB202503) |
| Indexed By | SCI |
| Language | 英语 |
| Funding Project | 多相选择氧化研究组 |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.licp.cn/handle/362003/1875 |
| Collection | 羰基合成与选择氧化国家重点实验室（OSSO） |
| Corresponding Author | Ji SF(季生福) |
| Recommended Citation GB/T 7714 | Hu LH,Ji SF,Jiang Z,et al. Direct synthesis and structural characteristics of ordered SBA-15 mesoporous silica containing tungsten oxides and tungsten carbides[J]. Journal of Physical Chemistry C,2007,111(42):15173-15184. |
| APA | 胡林华,季生福,江正,宋焕玲,武平一,&刘倩倩.(2007).Direct synthesis and structural characteristics of ordered SBA-15 mesoporous silica containing tungsten oxides and tungsten carbides.Journal of Physical Chemistry C,111(42),15173-15184. |
| MLA | 胡林华,et al."Direct synthesis and structural characteristics of ordered SBA-15 mesoporous silica containing tungsten oxides and tungsten carbides".Journal of Physical Chemistry C 111.42(2007):15173-15184. |
| Files in This Item: | ||||||
| File Name/Size | DocType | Version | Access | License | ||
| 84_J.Phys.Chem.C,200（617KB） | 开放获取 | License | View Application Full Text | |||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment